ZHF 82AT0

上一篇：ZHF 80AT3  下一篇：ZHF85AT3
Type: Noveon ® ZHF 82AT0 NAT021 is 82A aromatic Polyether-Based, Non-Halogen Flame Retardant, Thermoplastic Polyurethane (TPU) Compound
 
Feature: Soft, Matte finished, Good Flame Retardant Properties
 
Uses: Wire & Cable extrusion
 

Physical Properties

Value

Unit

Test Method

Hardness ( 3 sec)

82+/- 2

Shore A

ISO 868

Specific Gravity

1.13

g/mm3

ISO 2781

Tensile Strength

24.5

Mpa

ISO 527

Ultimate Elongation

620

%

ISO 527

Modulus at

 

 

 

50% Elongation

4.1

Mpa

 

100% Elongation

4.9

Mpa

 

300 % Elongation

8.2

Mpa

 

Tear Strength( Die C )

 

 

 

Nicked

50.1

KN/m

ISO 34-1B

Un-nicked

101.1

KN/m

ISO 34-1B

FR Property

 

 

 

UL 94 vertical burn

V0

---

UL94

Remark:  1. Prior to testing, samples were conditioned at 23oC for 24 hours
 
              2. Physical property test are based on 2mm molding plaques
 
              3. Please be aware that the listed data is a “typical data” which should / can not be applied for specification purpose
 
Materials Preparation:
 
Prior to process, Noveon ® ZHF 82AT0 NAT021 must be dried below 105°C for 3 hours. It is recommended to dry these materials in a dehumidifier, target dew point to be -30°C, preferable – 40°C.
 
Depending on the process technique, the maximum moisture content is recommended < 0.02%.
Process Condition:
 
Noveon ® ZHF 82AT0 NAT021 is extruded on any conventional extruder equipped with a PVC , 3 stage or barrier type screw having an L/D ration of 25:1 and a compression ratio of 3:1
 

 

oC

Hopper

Cooling

Zone 1

160

Zone 2

170

Zone 3

175

Zone 4

180

Adapter ( 5)

180

Die (6)

175

Dip tip (7)

170


ZHF 82AT0 Physical property table download